| dc.description | Resumen
Los compósitos de P3HT/NCC y P3HT/SiO2 se sintetizaron a través del método in-
situ y ex-situ usando diferentes razones en peso P3HT/NCC (75/25,50/50, 25/75 y
5/95) y P3HT/SiO2 (99/1,97/ 3, 95/5, 90/10, 80/20, 50/50, 25/75 y 5/95).
Para conocer el efecto de la incorporación de SiO2 y NCC en P3HT y las
propiedades fisicoquímicas que poseen los compósitos obtenidos, se
caracterizaron mediante FTIR, UV-Vis, RDX, TGA, voltametría cíclica y FE-SEM.
FTIR reveló la incorporación e interacción física de SiO2 y NCC en P3HT. Los
resultados de la caracterización revelaron que los compósitos P3HT/NCC
presentan un orden cristalino, la degradación térmica de NCC se ve mejorada y
muestran propiedades electroquímicas y ópticas interesantes. Por otro lado, la
estabilidad térmica del P3HT en los compósitos P3HT/SiO2 se vio mejorada. Estos
compósitos también presentaron actividad electroquímica y un orden cristalino. Es
interesante encontrar que para el compósito P3HT/SiO2, el monómero 3HT
polimerizó incluso cuando el contenido de partículas inorgánicas fue alto (10 y
20%). La absorbancia de los compósitos en el espectro UV-Vis disminuye al
incrementar el contenido de partículas, por su parte, el band gap disminuye
ligeramente.
Las propiedades electrocrómicas, electroquímicas, térmicas y no tóxicas de los
compósitos P3HT/NCC y P3HT/SiO2 impulsan el interés para ser objeto de estudio
ya que sus características pueden ser explotadas e implementadas en diversas
aplicaciones como: biomédicas, dispositivos electrónicos y dispositivos de
almacenamiento de energía. | es_MX |
| dc.description | Abstract
The P3HT/NCC and P3HT/ SiO2 composites were synthesized through the in-situ
and ex-situ method using different P3HT/NCC weight ratio (75/25, 50/50, 25/75
and 5/95) and P3HT/SiO2 weight ratio (99/1, 97/3, 95/5, 90/10, 80/20, 50/50, 25/75
and 5/95) %.
To know the effect of the incorporation of SiO2 and NCC in P3HT and the
physicochemical properties of the obtained composites, they were characterized by
FTIR, UV-Vis, RDX, TGA, cyclic voltammetry and FE-SEM. FTIR revealed the
incorporation and physical interaction of SiO2 and NCC in P3HT. The results of the
characterization revealed that the P3HT/NCC composites present a crystalline
order; the thermal degradation of NCC is improved and they show interesting
electrochemical and optical properties. On the other hand, the thermal stability of
P3HT in P3HT/SiO2 composites was improved. These composites also showed
electrochemical activity and a crystalline order. It is interesting to find that for the
P3HT/SiO2 composite, the 3HT monomer polymerized even when the content of
inorganic particles was high (10 and 20 wt%). The absorbance of the composite in
the UV-Vis spectrum decreases with increasing particle content, for another hand,
the band gap decreased slightly. The electrochromic, electrochemical, thermal
and non-toxic properties of the P3HT/NCC and P3HT/SiO2 composites drive the
interest to be the object of study since their characteristics can be exploited and
implemented in several applications such as: biomedical, electronic devices and
energy storage devices. | es_MX |
| dc.format | pdf - Adobe PDF | es_MX |
| dc.language | spa - Español | es_MX |
| dc.publisher | El autor | es_MX |
| dc.rights | openAccess - Acceso Abierto | es_MX |
| dc.subject | 7 - INGENIERÍA Y TECNOLOGÍA | es_MX |
| dc.subject.other | 33 - CIENCIAS TECNOLÓGICAS | es_MX |
| dc.title | Síntesis y caracterización de compósitos poliméricos a base de P3HT y materiales naturales | es_MX |
| dc.type | doctoralThesis - Tesis de doctorado | es_MX |
| uaem.unidad | Centro de Investigación en Ingeniería y Ciencias Aplicadas (CIICAP) - Centro de Investigación en Ingeniería y Ciencias Aplicadas (CIICAP) | es_MX |
| uaem.programa | Doctorado en Ingeniería y Ciencias Aplicadas - Doctorado en Ingeniería y Ciencias Aplicadas | es_MX |
| dc.type.publication | acceptedVersion | es_MX |
| dc.audience | researchers - Investigadores | es_MX |
| dc.date.received | 2021-03-04 | |